Urea silicon product and uses thereof

ABSTRACT

This invention relates to urea containing silicon compounds of the formula

United States Patent Pepe et al. 1 Aug. 28, 1973 UREA SILICON PRODUCT AND USES OTHER PUBLICATIONS THEREOF Mironov et al., Reaction of Some Carbofunctional [75] Inventors. ESE Z AZZZi I Marsden' Compounds of Silicon with Phosgene," Zh. Obshch. Khim., v01. 36, 1966) p. 1860., (Chem. Abst. v01. 66, [73] Assignee: Union Carbide Corporation, New 65577 York, NY.

Filed: P 1972 Primary Examiner-William D. Martin [21] AppL No; 244,280 Assistant Examiner-William H. Schmidt Related US. Application Data Division of Ser. No. 759,524, Sept. 12, 1968, Pat. No.

3,671,562, Continuation-impart of Ser. No. 729,895, May 17, 1968, abandoned.

US. Cl. 117/72, 117/124 F, 117/126 GN, 117/161 ZA, 156/329 Int. Cl. B32b 17/10, B32b 27/06, C071 7/02 Field of Search 117/124 F, 161 ZA,

117/126 GN, 72; 260/4482 R, 448.2 N

Attorney-Paul A. Rose et al.

[57] ABSTRACT This invention relates to urea containing silicon compounds of the formula I o (nm i lzfi iz and the uses thereof, particularly as coupling agents on glass and to the similar use of substituted urea containing silicon compounds.

3 Claims, No Drawings UREA SILICON PRODUCT AND USES THEREOF This application is a division of copending application Ser. No. 759,524 filed Sept. 12, 1968 now US. Pat. No. 3,671,562, issued June 20, I972 in turn is a continuation in part of abandoned application Ser. No. 729,895 filed May 17, 1968.

This invention relates to new urea substituted siliconcontaining compositions of matter, processes for producing them, and their uses; as well as new uses for a variety of other urea substituted silicon-containing compounds.

One embodiment of this invention relates to new silicon compounds characterized by the presence of the following radical:

wherein at least one of the three free valences of the silicon atom are bonded directly to hydrolyzable groups such as alkoxy, acyloxy, aryloxy, amino, and the like and/or oxygen which in turn is bonded to other silicon atoms to form a siloxane. The remaining free valences of the silicon atom are bonded by carbon to silicon bonds to monovalent organic groups. In the above formula I, R is an alkylene radical containing at least three carbon atoms and at least 1 nitrogen atom therein bonded to each (I-I,NCO-)- to form (II NCON at least one (1) free valence of is bonded to an alkylene carbon atom of R, any other free valences thereof are bonded to either hydrogen, alkyl, aryl, cycloalkyl, aralkyl, and the like; any nitrogen in R is separated from silicon by at least three sequential carbon atoms; and n is at least I and typically not greater than about 3.

Specifically illustrative of such area substituted silicon compounds are those depicted by the following formula:

wherein R and n are described above, R is any monovalent organic group bonded to silicon by a carbon to silicon bond and typically contains not more than about 12 carbon atoms; R can be hydrogen and/or R; R is a hydrolyzable and/or condensible radical such as hydroxyl, alkoxy, aryloxy, acyloxy and the like; R is hydrogen, alkyl aryl, acyl and the like; m is or I; a is 0, 1 or 2; bis(), 1, 2 or 3;0 isOor l;pis equal to 3-a when m is 0, and when m is l, p is 0; and q is 0 when p is equal to 3-a and q is 0 or a positive number when m is I.

Illustrative of R is any monovalent organic radical such as alkyl (e.g., methyl, ethyl, pentyl, dodecyl, octadecyl, 2-ethylhexyl, and the like), cycloalkyl (such as cyclobutyl, cyclohexyl, 4-methylcyclohexyl, and the like), aryl (such as phenyl, 2-naphthyl, Z-anthracyl, biphenyl, and the like), alkaryl (such as 4-methylphenyl,

2,4-diethylphenyl, 4-dodecylphenyl, and the like), aralkyl (such as phenylethyl), alkenyl (such as vinyl, allyl, 3-butenyl, oleyl, and the like), alkadienyl (such as lbutadienyl-l,4,l-octadecatrienyl-9, ll, 13-, lneoprenyl, and the like), cycloalkenyl (such as 3- cyclohexenyl), haloalkyl (such as chloromethyl, gamma-chloropropyl, 3,3,3-trifluoropropyl, perfluoropropyl, haloaryl (such as 4-chlorophenyl, 2,4- dichlorophenyl, chloronaphthyl), halocycloalkyl (such as 4-chlorocyclohexyl), cyanoalkyl (such as betacyarioethyl, gamma-carboxypropyl and the like); cyanoaryl (such as 4-cyanophenyl); cyanocycloalkyl (such as 4-cyanocyclohexyl, 3-cyanocyclopentyl, and the like); carboxyalkyl (such as beta-carboxyethyl, gamma-carboxypropyl, and the like); carboxyaryl (such as 4-carboxyphenyl); carboxycycloalkyl (such as 4-carboxycyclohexyl, 3-carboxycyclopentyl, and the like; isocyanatoalkyl (such as gammaicocyanatopropyl, delta-isocyanatobutyl, and the like); isocyanatoaryl (such as 4-isocyanatophenyl); isocyanatocycloalkyl (such as 4-isocyanatocyclohexyl); alkyl or aryl carboxyalkyl (such as betamethylcarboxyethyl, gamma-phenyl carboxypropyl, and the like); hydroxyalkyl (such as hydroxymethyl, gamma-hydroxypropyl, and the like); hydroxy(polyalkyleneoxy)alkyl (suchas omegahydroxy(polyethyleneoxy)propyl, and the like); alkenoyloxyalkyl (such as gamma-acrylyloxypropyl, gamma-methacryloxypropyl, and the like); epoxyalkyl (such as 1,2-epoxyethyl, 1,2-epoxypropyl, 1,2 epoxybutyl, and the like); epoxy alkyloxyalkyl (such as glycidyl-oxypropyl); epoxycycloalkyl (such as beta- 3,4-epoxycyclohexylethyl); aminoaryl and aminoalkyl (such as aminomethyl, gamma-aminopropyl, deltaaminobutyl, p-aminophenyl, and the like); and the like.

Illustrative of alkoxy, acyloxy, aryloxy, amino, and the like, such as mentioned above and characterized by R or R when q is a positive number, are for example methoxy, ethoxy, propoxy, dodecyloxy, isopropoxy, and the like; phenoxy, naphthyloxy, biphenyloxy, and the like, alkylamino and arylamino (such as methylamino, diethylamino, phenylamino, and the like), formyloxy, acetyloxy, proprioxy, and the like, any organo-functional radicals such as hydroxyalkoxy (such as beta-hydroxyethoxy, gamma-hydroxy-propoxy, and the like); hydroxyalkoxyalkoxy (such as betahydroXyethoxy-ethoxy, omega-hydroxy (polyethyleneoxy)ethoxy, omega-hydroxy (poly- I ,2- propyleneoxy), and the like; cyanoalkoxy (such as beta-cyanoethoxy, beta-cyanohexoxy and the like); cyanoalkoxyalkoxy (such as beta-cyanoethoxyethoxy, omega-cyanoethoxy (polyethyleneoxy), omegacyanoethoxy(poly-l,2-propyleneoxy), and the like); carboxyalkoxy (such as beta-carboxyethoxy, betacarboxyhexoxy and the like); haloalkoxy (such as chloromethoxy, bromoethoxy perfluoropropoxy, and the like); and the like.

The products of this invention may be produced by the treatment of silanes or siloxanes characterized by the following formula:

wherein the hydrogen which is present 11 times in formula III is bonded to the nitrogen referred to previously with respect to the definition of R; or

IV h.

wherein R is a divalent alkylene radical of at least three carbon atoms and which separates the isocyanato group from silicon by at least three sequential carbon atoms; and R R R, R, n, m, a, b, 0, p, and q are described above.

The treatment of the silanes or siloxanes characterized by formulae III and IV are different in order to make the ureas of formulae I and II. The amine of formula III is converted to urea by the reaction of the silanes of siloxanes of formula Ill with an organocarbamate such as alkyl, cycloalkyl or aryl carbamates illustrated by methyl carbamate, ethyl carbamate, and npropyl carbamate, n-butyl carbamate, cyclohexylcarbamate phenyl carbamate, 4-methylphenyl carbamate, 4-dodecyl phenyl carbamate, biphenyl carbamate; and alkylene, cycloalkylene and arylene carbamates, such as ethylene dicarbamate, 1,4-butylene dicarbamate, 1,4-phenylene dicarbamate, 4,4'-bisphenylene dicarbamate, 1,4-cyclohexylene di-carbamate, and the like. The reaction can be carried out neat or in solution or dispersion using solvents or nonsolvents for the silane and/or the carbamate reactants. Types of solvents and nonsolvents include water, hydrocarbon solvents, ether solvents, amide solvents, ketone solvents and the like, such as mineral spirits, hexane, n-nonane, benzene, toluene, xylene, methylethyl ketone, methylisobutyl ketone, diethylether, di-n-diisopropyl ether, N,N,- dimethyl formamide, and the like. The temperature of the reaction can be relatively low depending upon the reactivity of the carbamate and the amount of aminepresent in the reaction, usually temperatures in the range of about 40C. to about 180C. are satisfactory. Typically a temperature about 50C. to about 150C. is more desirable.

This reaction can be operated under atmospheric or subatmospheric pressures. Superatmospheric pressures are employable but are not considered to operate as beneficially as subatmospheric and atmospheric pressures. The reaction product can be separated by distillation, crystallization, decantation, and the like, utilizing standard processing equipment and procedures.

The treatment of an isocyanato silicon compounds of formula IV to produce the urea involves the reaction of ammonia with the isocyanate. This reaction can proceed at exceedingly low temperatures, viz., as low as 75C., or lower, typically at least 50C., and usually not greater than about 150C. The reaction also can be performed neat or in admixture either by dissolution or suspension of either one or both of the reactants in a solvent or nonsolvent, as the case may be. Usually, the isocyanate or formula IV is liquid, most desirably in solution, and the ammonia is bubbled through the solution as a gas or is employed in liquid form. In the preferred process, the isocyanate is reacted with liquid ammonia. This minimizes the use of Superatmospheric pressure as is required when using gaseous ammonia.

This invention also contemplates a number of other embodiments, particularly the utilities of the aforementioned ureas as well as ureas characterized by the following formula:

wherein R, R, R R, R, n, a, b, m, o, p, and q, are described above, and R may be alkyl or aryl, such as de scribed above,provided at least one R is hydrogen or methylol, or both R s may be methylol, i.e., (CH- Ol-l). These materials may be formed by reacting the product of formula ll with an alkyl or aryl halide to add one alkyl or aryl group or by reacting aryl or alkyl amines with the isocyanate or formula IV or by reacting N-alkyl or N-aryl carbamate esters with the amine of formula Ill. The methylol substituted areas may be formed by simple dissolution or dispersion of silanes or siloxanes characterized by formula II is aqueous formaldehyde solution, or by direct reaction of fonnaldehyde or its precursors, to wit, hexamethylenetetraamine or trioxane in a non-aqueous solvent solution of the silane or siloxane. Conventional art recognized reaction conditions may be employed.

The amines which may be treated in accordance with the process of this invention are those which are described in US. Pat. No. 2,971,864, patented Feb. 14, 1961, specific embodiments being illustrated in examples l, 2, 3, 4 and 6 thereof; US. Pat. No. 2,832,754, particularly at Examples 1, 2, 3 and 4 thereof; and US. Pat. No. 2,942,019 at columns 1,2,3 to lines 17 of column 4 with respect to silanes and siloxane homopolymers and copolymers which are described therein to be reacted with aldehydes and ketones.

It has been found that the above ureas, used as aqueous solutions of the hydrolyzates of the aforedescribed urea substituted silanes of formulas II and V, or the partially condensed to totally condensed siloxanes of formulas II and V employed neat or in solution, can be most effective coupling agents, particularly on fiber glass for further reaction with a board variety of thermosetting and/or thermoplastic resins. They can be added first onto the glass followed by treatment with the resin or they can be premixed with the resin and added to glass. In any event, it is found that these silanes and siloxanes supplied to the glass surface to form a siloxane coated thereon act to strongly adhere resin either simultaneously or thereafter supplied to the glass. Illustrative of resins which can be effectively bonded include the thermosetting resins, such as the phenol formaldehyde, melamine-formaldehyde, polyester resins, such as those formed by the reaction of ethylene glycol, maleic acid or anhyd'ride with or without styrene monomer and/or polymer, alkyd resins, polyurethane resins, epoxy resins, and the like. It may also be used to couple thermoplastic resins which possess reactive groups, such as isocyanate, carboxy, epoxy, and the like, by the inclusion in the resin of a catalyst for enhancing the reaction such as the well known metal catalysts, e.g., tin octoates, alkyl tin compounds, lead, cobalt, manganese, zinc, titanate and the like, driers and catalysts to enhance the reaction to the urea siloxane with the resin on the glass fiber surface. Also there may be included in the resins peroxide and hydroperoxide catalysts for the resins to achieve theoretical formation of fragments for the urea siloxanes on the glass surface which add to the resin and vice versus. Resins which most suitably respond to this type of reaction system include the thermoplastics, such as polyethene, polypropylene, copolymers of ethylene and propene, polyvinylchloride, polyvinylbutyral, polyacrylonitrile, copolymers or styrene and acrylonitrile, copolymers of styrene and butadiene-l ,3, copolymers of acrylonitrile and vinylchloride, and the like. The invention is particularly useful in this area in enhancing the bonding of polyvinylbutyral resin to plate glass in the manufacture of plate glass laminates. The urea substituted siloxanes also act as effective coupling agents on other inorganic substrates such as siliceous pigments and fillers, e.g., clay, silica, hydrated silica, fumed silica, sand and the like. The silanes are most effectively employed in treating sand which can be employed in foundry molding using hot or cold curing resins of the phenolformaldehyde, resorcinol-formaldehyde, and melamine-formaldehyde type. These ureas substituted siloxanes enhance the bonding of the resin to the sand.

EXAMPLE 1 a. Ammonia Method Into a 1-liter, 3-necked flask fitted with dry-ice condenser, thermometer, magnetic stirrer and dropping funnel is charged about 100 ml. of liquid ammonia. Over a period of 30 minutes, 205,3 grams (1.0 moles) of 'yOCN(CH Si(O Me) is added, dropwise with stirring. External cooling with a dry-ice and acetone bath is used to maintain a reaction temperature of 30 to 40C. The excess ammonia is removed by sparging with dry nitrogen over a period of 1 hour. A vacuum strip to 80C./ mm. produces the clear, colorless and somewhat viscous urea derivative,

in near quantitative yields.

Infrared spectral survey is in arrangement with the assigned monosubstituted urea structure. calc for C 1-1,,,SiO.,l 1 37.8% C; 8.2% H; 12.6% Si; 12.6% N; 41.9% OMe. Anal. 38.1, 8.1, 12.7, 12.2, 39.6.

b Transesterfication Method Into a 500 ml. distillation flask outfitted with thermometer and attached to a ldistillation Vigreaux column, distillation head and receiver is charged 110.5 gms. (0.5 moles) of 'y-Nl-l (C11 Si(O E0 44.5 gms. (0.5 moles) of CIhCIIgOCNlIg and 250 ml. of toluene. Titration of the total mixture in isopropyl alcohol, using standardized 0.1N HCl and brom cresol green indicator, shows the presence of 1.71 meg. of NH, per ml. The reaction mixture is heated to reflux at 130C. while removing 5 ml. of distillate boiling at from 105 to 110C. at atmospheric pressure over 1 hour. Retitration of the total reaction mixture indicates 1.64 meg/ml. of NH,. At this point, 0.5 gms. of dibutyltin oxide is added and reflux continues for 3 hours during which time 186 gms. ofa 83 percent toluene 15.1% EtOH(ethanol) mixture is removed at the head, boiling at from 105 to 1 10C. at atmospheric pressure. Removal of the balance of toluene and ethanol by vacuum stripping to 100C. at 1 mm. mercury pressure produces 138.4 gms. (104 weight ercent of calculated yield) of crude containing 0.03 meg/ml. of residual -Nl-l (94 mole percent conversion). Infrared spectral survey verifies the presence of monosubstituted urea structure. Aside from the expected differences due to triethoxysilicon groups, the major absorption characteristics are identical to those obtained from the product of Example 1a.

EXAMPLE 2 Composites were prepared as follows: 500 grams of glass beads range in sizes from 325 to 40 mesh, U.S. Standard, are mixed with 30.9 grams of a 50 per cent aqueous solution of methylol rich A-stage phenolforrnaldehyde resin (approximately 3 weight per cent resin solids based on weight of glass beads), 0.9 gram of concentrated aqueous NH OH solution, 7.7 grams of water and 0.016 grams of silane (0.1 weight per cent silane based on resin solids). This mixture is placed in a multiple cavity dumbbell shaped mold and cured for 7 min. at 450F. to produce a cured article of the mold shape The following table shows tensile strengths of a number of such molded articles, the differences between each being the use of silane as set forth in the table:

Tensile Strength Results Produced according to the following reaction: (CH,O);Si(CH,);N=C=O H,N(CH;),Si(OCl-l,),

CH,0),Si(CH,),,NHCONH(CH,);Si(OCl-l,), Produced according to the following reaction:

(CH O) Si(CH;);N=C=O+CH -,NH

(CH,0),Si(CH,),NHCONHCH, Produced according to the following reaction:

( r 11;()) i( Guam- 0:0 in: cm).

- ll HJO)3Si(CHQ)JNHCN(CH3) EXAMPLE 3 Into a 3-liter, 3-necked flask outfitted with thermometer, heating mantle, mechanical stirrer and a 12 inch Vigreaux column with distillation head and receiver is charged 1,100 gms. (5.0 moles) of NH,(CH,),NH(CH,),Si(OMe),, 375 gms. (5.0 moles) of methyl urethane, MeOOCNH, 908 gms. of anhydrous toluene and 3.9 gms. (0.25 wgt percent) of dibutyl tin oxide. The stirred mixture is heated at reflux from 96 to 119C for hours, during which time 751.9 gms. of distillate is removed boiling at from 64 to 109C at atmospheric pressure and determined by gas chromatographic analysis to contain approximately 24 volume percent methanol and 76 volume percent tolu- 5 ene. Exactly one half of the total reaction mixture is removed and stripped under acuum to 100C at 1 mm. of mercury pressure to produce 605 gms. (2.28 moles) in 91 mole percent yield.

EXAMPLE 4 To 605 grams (2,28 moles) of dissolved in 1400 gms. of toluene is added an additional 187.5 gms. (2.5 moles) of methyl urethane and the procedure discribed above is repeated to produce 668 gms. (2,17 moles) of light yellow, high viscosity o 0 NHZbNHwH NQ INHZ)(cnmsuoima in 9.54 mole yield.

EXAMPLE 5 In much the same manner as described in Example 3,590 gms. (6.0 moles) of NH (CH Nl-l(Cl-l NH(CH Si(OMe) is reacted with 450 gms. (6.0 moles) of MeOOCNl-l until 6 moles of by-product methanol has been formed and removed by distillation. One third of the total reaction mixture is removed and vacuum stripped to C/1.0 mm. to obtain 615.6 gms. (2.0 moles) of the mono-urea derivative,

a light yellow viscous syrup soluble in water, alcohols and toluene.

EXAMPLE 6 which is soluble in methanol, ethanol, isopropanol, water and toluene.

EXAMPLE 7 To the remaining di-urea derivative prepared in Example 6 is added gms. (2.0 moles) of MeOOCNH 500 ml of additional toluene and the transesterification reaction driven to completion in the same manner as described above. There results upon workup in the aforementioned manner a quantitative yield of the triurea derivative,

The latter is amine free, thermoplastic, clear orange, glass-like at room temperature and softens and flows at about 80C. and is soluble in alcohols (e.g., methanol, ethanol, etc.) and water.

As noted above, the urea silanes are extremely effective coupling agents and are notably useful in coupling or enhancing the bonding of fiber glass to a plurality of organic materials such as rubber, e.g., ethylenepropylene terpolymer rubbers and butadiene-styrene rubbers. These silane coupling agents offer exceptional promise as coupling agents in making fiber glass reinforced rubber tires and other rubber goods.

Me, as employed herein, means the methyl radical.

What is claimed is:

1. An inorganic substrate treated with a silicon compound having the formula:

wherein R is an alkylene radical containing at least 3 carbon atoms and at least 1 nitrogen atoms therein bonded to each (H NCO) to form at least one free valence of (ll NCON is bonded to a nitrogen containing alkylene carbonatom of R, any other free valence of (mNcoN is bonded to a member selected from the group consisting of hydrogen, alkyl, aryl, cycloalkyl and aralkyl, and nitrogen atom in R is separated from silicon by at least three sequentially joined carbon atoms, and n is at least one; R is a monovalent organic group bonded to silicon by a carbon to silicon bond; each R is hydrogen or R; R is a hydrolyzable or condensible radical; R is a member selected from the group consisting of hydrogen, alkyl, aryl and acyl; m is 0 or 1; a is O, 1 or 2; b is 0,1, 2 or 3; 0 is 0 or 1; p is equal to 3-a when m is 0, and when m is 1, p is O; and q is 0 when p is equal to 3-a and q is 0 or a positive number when m is 1.

2. The product of claim 1 wherein the substrate is made of glass.

3. In a composite of an inorganic substrate and an organic resin wherein the adhesion of said resin to said substrate is enhanced by a coupling agent, the improvement which comprises employing as said coupling agent a silicon compound containing the radical wherein at least one of the individual free Si valences are bonded directly to a hydrolyzable group, selected from the group consisting of alkoxy, acyloxy, aryloxy, amino and haloalkoxy, or oxygen which in turn is bonded to another silicon atom to form therewith a siloxane, and the remaining free valences are bonded by carbon to silicon bonds to monovalent organic groups selected from the group consisting of alkyl, cycloalkyl, aryl, alkaryl, aralkyl, alkenyl, alkadienyl, cycloalkenyl, haloalkyl, halocycloalkyl, cyanoalkyl, cyanoaryl, cyanocycloalkyl, carboxy-alkyl, carboxyaryl, carboxycycloalkyl, isocyanatoaryl, isocyanatocyloalkyl, alkyl carboxyalkyl, aryl carboxyalkyl, hydroxyalkyl, hydroxy (polyalkyleneoxy)alkyl, alkenoyloxyalkyl, epoxyalkyl, epoxy alkyloxyalkyl, aminoaryl and aminoalkyl, R is a nitrogen containing alkylene radical containing at least three carbon atoms and at least one nitrogen atom therein bonded to each (H,NCO-)- to form at least one free valence of (H NCON is bonded to an alkylene carbon atom of R, any other free valence of (rnNcoN one.

UNlTED STATES PATENT OFFICE CERTIFICATE OF CORRECTION.

Patent No. 3,754,971 Dated August 28, 1973 Inventor(s) E1 'lricO J. Pepe et al It is certified that error appears in the above-identified patent and that said Letters Patent are; hereby corrected as shown below:

Column 4, line 10, 'areals" should read --ureas-- line 12, "is" shouldread. --in--. Column 5, line 34, "arrangement" should read -agreement--. Column 6, line 28, "256" should read --265r;-1ine 30, that portion of the formula reading:

H v H MCI-I should read N(CH Column 7, line 31,

I "9.54" should ead 95.4--; line 53, MeOOCI-I should read meoocuuz Signed and sealed this 26th day of November 1974.

(SEAL) Attest:

McCOY M; GIBSON JR. 7 c. MARSHALL DANN Arresting Officer Commissioner of Patents F RM 80- 05 I USCOMM-DC scan-p69 I v "l5. GOVERNMENT PRIN'HNG OFFICE 2 l9. 0-355-33, 

2. The product of claim 1 wherein the substrate is made of glass.
 3. In a composite of an inorganic substrate and an organic resin wherein the adhesion of said resin to said substrate is enhanced by a coupling agent, the improvement which comprises employing as said coupling agent a silicon compound containing the radical 